Compress Sintering
stainless range powder
|
|
| shop
sign |
Chemistry
ingredient(%)
|
Apparent
Density
(g/cm3)
|
Flow
Rate (s/50g)
|
Granularity
Distribution (%)
|
|
Cr
|
Ni
|
Mo
|
Mn
|
Si
|
C
|
P
|
S
|
O
|
Fe
|
spec
|
content
|
| 304L |
18-20 |
9-12 |
\ |
0.2 |
0.8 |
≤0.03 |
≤0.03 |
≤0.02 |
≤0.3 |
spare |
2.5-2.8 |
33-38
|
+100mu
|
<2
|
|
-325mu
|
40-60
|
| 316L |
16-18 |
12-15 |
2-3 |
0.2 |
0.8 |
≤0.03 |
≤0.03 |
≤0.02 |
≤0.3 |
spare |
2.5-2.8 |
33-38
|
+100mu
|
<2
|
|
-325mu
|
40-60
|
| 317L |
18-20 |
12-15 |
3-4 |
0.2 |
0.8 |
≤0.03 |
≤0.03 |
≤0.02 |
≤0.3 |
spare |
2.5-2.8 |
33-38
|
+100mu
|
<2
|
|
-325mu
|
40-60
|
| 410L |
12-13 |
\ |
\ |
0.2 |
0.8 |
≤0.03 |
≤0.03 |
≤0.02 |
≤0.3 |
spare |
2.5-2.8 |
33-38
|
+100mu
|
<2
|
|
-325mu
|
40-60
|
| 430L |
16-17 |
\ |
\ |
0.2 |
0.8 |
≤0.03 |
≤0.03 |
≤0.02 |
≤0.3 |
spare |
2.5-2.8 |
33-38
|
+100mu
|
<2
|
|
-325mu
|
40-60
|
| 434L |
17-18 |
\ |
1.0-1.5 |
0.2 |
0.8 |
≤0.03 |
≤0.03 |
≤0.02 |
≤0.3 |
spare |
2.5-2.8 |
33-38
|
+100mu
|
<2
|
|
-325mu
|
40-60
|
|
420L
|
12-14
|
|
|
≤1.00
|
≤1.00
|
0.26-0.40
|
≤0.040
|
≤0.030
|
≤0.3
|
余
|
2.5-2.8
|
33-38
|
-325目
|
40-60
|
|
| |
| |
stainless powder
for injection moudling alloy steel powder
|
|
| shop sign |
Chemistry
ingredient(%)
|
振实密度(g/cm3)
|
Average
Density (μm)
|
Granularity
Distribution (%)
|
|
Cr
|
Ni
|
Mo
|
Mn
|
Si
|
C
|
P
|
S
|
O
|
Fe
|
| 304L |
18-20 |
9-12 |
\ |
0.2 |
0.8 |
≤0.03 |
≤0.03 |
≤0.02 |
≤0.3 |
spare |
3.3-3.9
|
≤25
|
2-30μm
|
| 316L |
16-18 |
12-15 |
2-3 |
0.2 |
0.8 |
≤0.03 |
≤0.03 |
≤0.02 |
≤0.3 |
spare |
3.3-3.9
|
≤25
|
2-30μm
|
| 317L |
18-20 |
12-15 |
3-4 |
0.2 |
0.8 |
≤0.03 |
≤0.03 |
≤0.02 |
≤0.3 |
spare |
3.3-3.9
|
≤25
|
2-30μm
|
| 410L |
12-13 |
\ |
\ |
0.2 |
0.8 |
≤0.03 |
≤0.03 |
≤0.02 |
≤0.3 |
spare |
3.3-3.9
|
≤25
|
2-30μm
|
| 9Gr18 |
17-19 |
\ |
\ |
0.2 |
0.8 |
0.9-1.0 |
≤0.035 |
≤0.03 |
≤0.3 |
spare |
3.3-3.9
|
≤25
|
2-30μm
|
|
| |
| |
alloy steel powder
|
|
| shop sign |
Chemistry
ingredient(%)
|
Apparent
Density
(g/cm3)
|
Flow
Rate (s/50g)
|
Granularity
Distribution (%)
|
|
Cr
|
Ni
|
Mo
|
W
|
V
|
Co
|
Nb
|
Cu
|
c
|
Fe
|
remark |
spec
|
content
|
| HAPM2 |
4-5 |
\ |
4.5-5.5 |
5.5-6.5 |
1.5-2.5
|
\
|
\
|
\
|
0.8-1.0 |
spare |
Cmix |
2.3-2.7 |
30-35
|
+100mu
|
<1
|
|
-325mu
|
40-60
|
| HAPT15 |
4-5 |
\ |
\
|
12.0-13.0
|
4.5-5.5
|
4.5-5.5
|
\
|
\
|
1.5-2.0
|
spare |
Cmix |
2.0-2.5 |
33-38
|
+100mu
|
<1
|
|
-325mu
|
40-60
|
| HAPNb1 |
11-14 |
\ |
1-2 |
\
|
\
|
\
|
3-5
|
\
|
≤0.05
|
spare |
\ |
\ |
\ |
+100mu
|
<1
|
|
-325mu
|
40-60
|
| HAPDH1 |
0.1-0.3 |
0.5-0.9 |
0.4-0.7 |
Mn0.2-0.4 |
\
|
0.3-0.5 |
\
|
0.3-0.5 |
1.5-2.0
|
spare |
Cmix |
2.5-3.0 |
35-40
|
+100mu
|
<1
|
|
-325mu
|
40-60
|
|